Offering fast and affordable ASTM A Jominy End Quench Test of Hardenability along with heat treating and metallurgy expertise. This standard is issued under the fixed designation A ; the number 1 These test methods are under the jurisdiction of ASTM Committee A01 on. Steel. ASTM A Determining Hardenability of Steel – Designation: A – 99 An American National S.

Author: Volmaran Goltiktilar
Country: Cayman Islands
Language: English (Spanish)
Genre: Education
Published (Last): 17 March 2011
Pages: 93
PDF File Size: 14.70 Mb
ePub File Size: 5.32 Mb
ISBN: 753-6-66184-454-9
Downloads: 42037
Price: Free* [*Free Regsitration Required]
Uploader: Kigrel

It is measured quantitatively, usually by noting the extent or depth of hardening of a standard size and shape of test specimen in a standardized quench. If the specimen is not cold when removed from the? Plating and Coating Testing.

This may be accomplished by heating the specimen in a vertical position in a container with an easily removable cover containing a layer of cast-iron chips with the bottom face of the specimen resting on the chips. The two hardness surveys are made on adjacent?

It is astm a quantitatively, usually by noting the extent or depth of hardening of atsm standard size and shape of test specimen in a standardized astm a Immerse in solution No. This testing can be done on a sub-sized sample which does not meet the standard size bar dimension as governed by Appendix X1.

  GABINETES RITTAL PDF

ASTM A255 Jominy Hardenability Testing

Then place the heated specimen in the support so that its bottom face is 0. Subscription pricing is determined 2a55 Carbon and Sulfur Analysis. Resting the specimen in a V-block is not permitted.

For simplicity, the DI should be rounded to the nearest 0. It has been found that with reasonable operating care and a well-built?

ASTM A – 02 Standard Test Method for Determining Hardenability of Steel

In cases of lack of reproducibility or of differences between laboratories, indenter spacing should be measured immediately. This test astm a assures that the astm a you are using is going to respond correctly to heat treatment. Rockwell or Superficial Hardness. Shallower ground depths can affect reproducibility of results, and correlation with cooling rates in quenched bars. If the standard hardenability curve is needed, then the insert test specimen shown in Fig.

This standard a2555 not purport to address all of the safety concerns, if any, associated with its use. Cast specimens are not suitable for boron steel grades due to erratic results.

Wilson Hardness Conversion Chart. It is the responsibility of the user of this standard to establish appropriate safety astm a health practices and determine the applicability of regulatory limitations prior to use.

  BOSS FV-50H PDF

G2MT Laboratories

A graphite or metal mold may be used to form an overlength specimen 1. After the quench, warm the assembly in boiling water to melt the Woods metal and remove the specimen.

If such changes caused by grinding are indicated, new? A — 99 Determinin Already Subscribed to this document.

Jominy Test ASTM A – Colorado-Metallurgical-Services

Jominy Testing This testing is indented for determining astj hardenability of astm a It is important to heat the specimen in such an atmosphere that practically no scaling and a minimum of decarburization takes place.

This standard is also available to be included in Standards Subscriptions. For comparison of this test method to others, or for steel compositions outside the mentioned sstm, the user should refer to other articles concerned with calculating hardenability.

We have no amendments or corrections for this standard. The specimen shall be machined from aztm bar previously normalized in accordance with 6. Normalizing may be waived by agreement between the supplier and the user.