AHM E8/E8M – 13a. G–Gauge length. Dimensions, mm [in.] For Test Specimens with Gauge Length Four times the Diameter (E8]. Standard. Small-Size. Buy ASTM E 8/E8M: A TEST METHODS FOR TENSION TESTING OF METALLIC MATERIALS from SAI Global. Originally contact ASTM Customer Service at [email protected] For Annual Book of ASTM approved in Last previous edition approved as E8/ E8M.

Author: Moshura Dailrajas
Country: Namibia
Language: English (Spanish)
Genre: Environment
Published (Last): 15 April 2012
Pages: 378
PDF File Size: 2.36 Mb
ePub File Size: 19.62 Mb
ISBN: 543-2-52999-150-9
Downloads: 50861
Price: Free* [*Free Regsitration Required]
Uploader: Faesar

Such interpretation is usually applicable to values for reduction of area reported in the literature when no further qualification is given.

This error increases to 2. For measuring elongation at fracture with an appropriate extensometer, the 8e length of the extensometer shall be equal to the nominal gauge length required for the specimen being tested. NOTE 1—The effect of this eccentric force application may be illustrated by calculating the bending moment and stress thus added. For a standard Originally approved in This information asym be useful in comparisons of materials, alloy development, quality control, and design under certain circumstances.

The distance between spherical bearings should be as great as feasible. Extensometers shall be used and verified to include the strains corresponding to the yield strength and elongation at fracture if determined.

For this reason, a small taper is permitted in the reduced section of each of the specimens described in the following sections. If, however, for any reason, one grip of a pair advances farther than the other as the grips tighten, an undesirable bending stress may be introduced. Current edition approved May 1, Combining values from the two systems may result in non-conformance with the standard. Parte 1 de 8 Designation: To ensure axial tensile stress within the gauge length, the axis of the test specimen should coincide with the center line of the heads of the testing machine.

  FIDIC EPC SILVER BOOK PDF

For short specimens and for specimens of many materials it is generally necessary to use machined test specimens and to use a special means of gripping to ensure that the specimens, when under load, shall be as nearly as possible in uniformly distributed pure axial tension see 5. A number in parentheses indicates the year of last reapproval.

ASTM E8.E8M -15-Tensiont testing of metallic materials

Proper alignment of wedge grips e8k liners is illustrated in Fig. For proper gripping, it is desirable that the entire length of the serrated face of each wedge be in contact with the specimen. For best results, the wedges should be supported over their entire lengths by the heads of the testing machine.

The gauge length is the most significant difference between E8 and E8M test specimens. The forces used in determining tensile strength and yield strength shall be within the verified force application range of the testing machine as defined in Practices E4.

Brittle Materials—A schematic diagram of a gripping device for threaded-end specimens is shown in Fig. Both of these gripping devices should be attached to the heads of the testing machine through properly lubricated sphericalseated bearings. These wedge grips generally furnish a satisfactory means of gripping long specimens of ductile metal.

Any departure from this requirement may introduce bending stresses that are not included in the usual stress computation force divided by cross-sectional area. A superscript epsilon indicates an editorial change since the last revision or reapproval.

  CONTRAPUNTO PISTON WALTER PDF

ASTM E8.E8M Tensiont testing of metallic materials –

C39M – 16 – Compressive Strength of Cylindrical No further reproductions authorized. It is important, therefore, that care be exercised in the preparation of specimens, particularly in the machining, to maximize precision and minimize bias in test results.

NOTE 3—Punching or blanking of the reduced section may produce significant cold work or shear burrs, or both, along the edges which should be removed by machining.

The test methods have been used aatm in the trade for this purpose. Astm c astm normas fibra de vidrio.

ASTM E8 / E8M – 13 Standard Test Methods for Tension Testing of Metallic Materials

Astm a Astm a It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. This requires that liners of several thicknesses be available to cover the range of specimen thickness. The values stated in each system are not exact equivalents; therefore each system must be used independently of the other.

E8M Tensiont testing of metallic materials Juliano row Enviado por: When liners are used behind the wedges, they must be of the same thickness and their faces must be flat and parallel.